Kinetics of phase transformations in glass forming systems

A nucleation rate like curve for a glass can be determined from the functional dependence of the maximum height of its DTA crystallization peak, (delta T)(sub p), on the nucleation temperature, T(sub n). This nucleation rate curve provides information for the temperature range where nucleation for the glass can occur and the temperature where the nucleation rate is a maximum. However, this curve does not provide information for the nucleation rate, I, for the glass at different temperatures. A method for estimating I at different temperatures from (delta T)(sub p) was developed using a Li2O.2SiO2 (LS2) glass. Also, the dielectric constant (epsilon) and the loss factor (tan delta) of a glass-ceramic depend, in part, upon the amount of crystallinity which, in turn, depends upon the nucleation density in the starting glass. It is therefore expected that epsilon and tan delta should have a relationship with nucleation density and hence on the nucleation rate.