Introduction of artificial pinning centres in Bi2Sr2CaCu2O8 ceramics

Considering the phase equilibrium diagram of the system Bi203-SrO-CaO-CuO, single phase 'Bi2Sr2CaCu208' ceramics have been transformed by a simple annealing procedure into multiphase samples. The transformation results in the formation of second phases and in an increase of the intra-grain critical current density at 1 T of five times. This increase is believed to express improved pinning properties of the superconducting crystals. The prepared pinning centers are believed to be e.g. coherent precipitates (Guinier-Preston-zones) within the superconducting crystals.