Tribological evaluation of PS300: A new chrome oxide based solid lubricant coating sliding against Al2O3 From 25 to 650 C

This paper presents the tribological characteristics of Al203 sliding against PS300; a chrome oxide based self lubricating coating. Al203 pins were slid against PS300 coated superalloy disks in air, under a 4.9 N load at velocities of 1 to 8 m/s. At a sliding velocity of 1 m/s, friction ranged from 0.6 at 25 C to 0.2 at 650 C. Wear factors for the Al203 pins were in the 10(exp -7) mm(exp 3)/N-m range and for the PS300 coating was in the 10(exp -5) mm(exp 3)/N-m range. The test results suggest that increased surface temperature resulting from either frictional heating, generated by increased sliding velocity, or ambient heating caused a reduction in friction and wear of the sliding couple. Based upon these results, the tested material combination is a promising candidate for high temperature wear applications.