Hot Hydrogen Exposure Degradation of the Strength of Mullite

This study deals with the corrosion of near stoichiometric mullite (3Al2O3-2SiO2) by pure dry hydrogen gas. Exposure of the mullite samples was at temperatures of 1050 and 1250 C for times up to 500 hours. Preferential attack of the alumino-silicate glass present in the grain boundaries of the mullite occurred after 125 hours at 1250 C. Hydrogen scrubbing of the SiO2 from the glassy grain boundaries and the mullite grains yielded a porous alumina-rich surface. The room temperature strength increased after short exposure times at 1250 C (up to 125 hours), then decreased by 53 percent after exposure for 500 hours. At 1050 C, all exposure times (25 to 500 hours) decreased the strength. After 500 hours in hydrogen at 1050 C, the room temperature strength of mullite decreased 22 percent. We also observed a rapid 25 percent strength loss after short exposure times at 1050 C. This is attributed to the calcium/hydrogen assisted crystallization of the glassy, grain-boundary phase.