Synthesis, Structure, and Characterization of Cu4S10(4-methylpyridine)4

The title compound, Cu4S10(4-methylpyridine)(sub 4) (dot) 4-methylpyridine was prepared by three different reactions: the oxidation of copper powder by sulfur and the reaction of copper (I) sulfide (or CuBr (dot) SMe2) with excess sulfur, both in the coordinating solvent, 4-methylpyridine. Red crystals of the compound obtained by layering with hexanes were subjected to single crystal X-ray diffraction. The structure was refined to R = 0.026 and R(sub w) = 0.036 in a space group P1bar (No. 2), with Z = 2, a = 13.983 (2) A, b = 15.384 (2) A, c = 9.660 (1) A, alpha = 93.87 (1)deg., beta = 93.38 (1)deg., gamma = 99.78 (1)deg., V = 2037.9 (9) A(exp 3). The compound has approximate S(sub 4) symmetry and consists of two pentasulfide chains linking four Cu(I) ions, each with a corrdinating 2-methylpyridine. The infrared spectrum was dominated by absorption due to coordinated 4-methylpyridine with several low-energy peaks attributable to S-S stretches, which were also observed by Raman spectroscopy. A featureless electronic absorption spectrum yielded a single peak in the near ultraviolet upon computer enhancement (lambda = 334 nm, epsilon = 10,000), most likely an intraligand transition. Cyclic voltammetry indicates that the polysulfide complex undergoes irrversible oxidation and reduction at +0.04 and -0.34 V vs. SCE, respectively, at 298 K in 4-methylpyridine when swept at 20 mV/sec. The electrochemical behavior was unvaried even at sweep rates as high as 100 V/sec.