GLAS 532nm Optical Detector

This report documents fabrication and testing of 532nm optical detectors. Testing procedures included 532nm quantum efficiency, detector gain, and photon counting performance, in particular, photon counting efficiency. 532nm quantum efficiency was measured to be 36% to 39% for the detectors fabricated. Detectors with a GaAs APD anode had measured gains of 12,000 to 15,000 maximum. Photon counting efficiency for the detector with an APD anode was measured to be approximately 80% with a detector gain of 11,000. Measurements made on an identical detector, not fabricated under this contract, had a photon counting efficiency exceeding 90% with a gain of 13,000. A formula is derived in which the photon counting efficiency is determined by the system preamp noise and the peak single photon pulse height which is proportional to detector gain. This formula agrees well with the measured results and indicates that a detector gain of 15,000 is sufficient to provide a counting efficiency of 99.6%.