Measurements of Total Hemispherical Emissivity of Several Stably Oxidized Nickel-Titanium Carbide Cemented Hard Metals from 600 F to 1,600 F

The total hemispherical emissivity of several nickel-titanium carbide cemented hard metals have been measured over a temperature range from 600 F to l,600 F. A variety of cemented hard metals were obtained from the Kennametal Corporation. A brief discussion of the apparatus employed and the procedures used for this investigation is included. The results of the tests of specimens in the as-received and polished states indicate a nearly constant emissivity for each material tested over the temperature range considered and only slight differences in emissivity values for the different materials. Values obtained on the stably oxidized specimens range from 0.90 to 0.94 at 6000 F and o.88 to 0.92 at 1,600 F for the as-received specimens and from 0.82 to 0.89 at 600 F and 0.85 to 0.87 at 1,600 F for the polished specimens. The surface analysis of the oxidized materials as obtained by X-ray diffraction methods and metallographic techniques are presented as an aid to reproducing the surface on which these measurements were made.