Evaluation of Several Space Lubricants using a Vacuum Four-Ball Tribometer

The friction and wear behavior of seven space lubricants was investigated under boundary lubrication conditions using a vacuum four-ball tribometer. Three of the lubricants were perfluoropolyethers (143AC, S-200, and Z-25). Three were synthetic hydrocarbons (a multiply alkylated cyclopentane, 2001a), and a formulated version with an antiwear and an antioxidant additive (2001). The third hydrocarbon was an unformulated polyalphaolefin (PAO-100). An unformulated silahydrocarbon (SiHC) was also evaluated. Test conditions included: a pressure less than 6.7 x 10(exp 4) Pa, a 200 N load, a sliding velocity of 28.8 mm/sec (100 RPM), and room temperature (approx. 23 C). The wear rate for each lubricant was determined from the slope of wear volume as a function of sliding distance. The lowest wear rate (0.033 x 10(exp-9) cu mm/mm) was obtained with the silahydrocarbon. The formulated synthetic hydrocarbon had a wear rate off O.037 x 10(exp -9)cu mm/mm, which was a 36% reduction compared to the unformulated fluid. The polyalphaolefin had the highest wear rate of the non-PFPE fluids. Of the perfluoropolyethers (PFPEs), wear rates decreased by about 50% from Z-25 (1.7 x 10(exp -9)cu mm/mm) to S-200 (0.70 x 10(exp -9)cu mm/mm) to 143AC (0.21 x 10(exp -9)cu mm/mm).