Interactions Between Solidification and Compositional Convection in Alloys

This project combined theoretical and experimental ground-based studies of the interactions between convection and solidification of binary melts. Particular attention was focused on the alteration of the composition and microstructure of castings caused by convective flows through the interstices of mushy layers. Two different mechanisms causing convection were investigated. (i) Compositional, buoyancy driven convection is known to cause chimneys and freckles in directionally cast alloys on Earth. The analytical studies provide quantitative criteria for the formation of chimneys that can be used to assess the expediency of producing alloys in Space. (ii) Flow of the melt is also driven by the contraction (expansion) that typically occurs during change of phase. Such convection will occur even in the absence of gravity, and may indeed be the primary cause of macrosegregation during the production of alloys in Space. The studies will employed asymptotic methods in order to determine conditions for the stability of various states of solidifying systems. Further, simple macroscopic models of complete systems were developed and solved. These analytical studies were augmented by laboratory experiments using aqueous solutions, in which the convective flows could be easily observed and the effects of convection could be readily measured. These y experiments guided the development of the theoretical models and provided data against which the predictions of the models can be tested.