An Approach to Processable Polyimides

The use of polymer matrix composites (PMC's) in aircraft engines can lead to substantial weight savings over metals. This weight reduction correlates into better fuel economy, increased speed, and increased passenger load. Typically, high performance PMC's possess high thermal-oxidative stabilities (TOS) and high glass transition temperatures (Tg's) to withstand temperatures up to 316 C (600 F). One of the leading high temperature resins system available today is PMR-15 (Polymerization of Monomeric Reactants, MW=1500). This thermosetting polyimide utilizes addition curing through polymer endcaps which enables hand lay-up processing of carbon fiber composite parts with low void contents. However, the large amount of hand labor raises manufacturing costs and prohibits the use of PMR-15 in many aerospace applications. Resin Transfer Molding (RTM) provides an economical alternative, but it requires a melt Viscosity of less than 10(exp 3) centipoise (cP). This is much lower than the minimum melt viscosity of PMR-15 (about 10(exp 6) cP). To improve the processability of polyimides, the polymer backbone can be modified by incorporating flexible linkages, such as branching. bulky pendant groups, kinked structures, and twisted or non-coplanar moietes . The focus of this paper will be the introduction of non-coplanar biaryls into the PMR polyimide backbone to increase processability while maintaining high temperature performance.