Final Report

This cooperative agreement explored the novel polymerization of vinylsilane, alone and in combination with other alkenylsilanes, alkylsilanes, and/or crosslinking agents, using dimethyltitanocene as homogeneous catalyst. The reactions were found to be initiated photochemically under mild conditions, and no hydrogen gas was evolved when alkenylsilanes were polymerized. The polymers were found to have predominately a carbosilane-type backbone containing -SiH2-CH2-CH2-Si and -SiH2-CH(CH3)-Si type linkages. The mechanism of polymerization was found to be step-growth. Despite the relatively low molecular weight of the polymer (M(sub n) - 500 and M(sub W) - 1500), pyrolysis resulted in conversion to C-rich SiC ceramic in high char yields (-60%). Copolymerization with methylsilane resulted in higher chars and more crystalline polymer. Addition of crosslinking agents such as polybutadiene or methyltrivinylsilane increased the viscosity of the polymer produced and enabled application as coatings to fiber toes.