Fluorescence of Pentavalent Chromium in SiO2 Sol-Gel Glasses

Chromium ions are very attractive to optical spectroscopy and laser physics. It is well known that the first laser in the history is a ruby laser activated with Cr(3+). It was found in early nineties that Cr(4+) was also an interesting lasing ion in the near infrared, and various Cr(4+) lasers have been developed. Very recently, it was reported that Cr(2+) doped in CdSe crystals showed lasing action in the infrared. The above achievement have stimulated an interest in searching for Cr(5+) and investigating its optical properties. Cr(5+) is isoelectronic with Ti(3+) and V(4+), having electron configuration 3d1. Ti(3+) is the active center of commercial cw and femtosecond sapphire lasers, tunable in the range 680-1100 nm. V(4+) doped in YAlO3 and Al2O3 showed broad band emission near 635 nm. Although EPR results of Cr(5+) were reported, the optical properties were less studied. Herren et al. reported an observation of luminescence from Cr doped in SiO2 sol-gel glass. The luminescence spectrum was assigned to pentavalent ions in their first paper, and later it was identified to be the emission from the charge transfer transition of Cr(6+). The first observation of photoluminescence from octahedrally coordinated Cr(5+) in BaCaMg aluminate glasses was reported very recently. In this work, we report luminescence results of Cr doped SiO2 sol-gel glasses. The fluorescence spectra are very different from Herrens' results, and we believe it originates from pentavalent Cr.