The Growth of Low Band-Gap InAs on (111)B GaAs Substrates

Growth on the (111)B orientation exhibits a number of advantageous properties as compared to the (100) during the early stages of strained-layer epitaxy. In accordance with a developing model of nucleation and growth, we have deposited thin (60 A - 2500 A), fully relaxed InAs films on (111)B GaAs substrates. Although thicker InAs films are subject to the formation of twin defects common to epitaxy on the (111)B orientation, appropriate control of the growth parameters can greatly minimize their density. Using this knowledge base, InAs films up to 2 microns in thickness with improved morphology and structural quality have been grown on (111)B GaAs substrates.