The Tribological Properties of Several Silahydrocarbons for Use in Space Mechanisms

Silahydrocarbons are members of a relatively new class of liquid lubricants with great potential for use in space mechanisms. They are unimolecular species consisting of silicon, carbon, and hydrogen. They possess unique wear, viscosity, and volatility properties while retaining the ability to solubilize conventional additives. The tribological properties of several members of this class, including tri, tetra- and penta-compounds, are presented. These properties include: viscosity-temperature (ASTM D446), viscosity-pressure coefficient, vapor pressure, volatility, lubricant lifetimes, traction, reciprocating and four ball wear rates and bearing performance. Lubricant lifetimes were determined using a vacuum ball bearing simulator, the spiral orbit tribometer (SOT). Wear was measured using a Cameron Plint reciprocating tribometer and wear rates with a vacuum four ball tribometer. Conventional viscometry was used for viscosity-temperature measurements and a Knudsen cell for vapor pressure. Vacuum Thermogravimetric Analysis (TGA) was also used for volatility measurements. Pressure viscosity coefficients (a values) were estimated from EHL (elastohydrodynamic lubrication) film thickness measurements. Traction coefficients were measured with a twin disk traction rig. Bearing tests were performed in a vacuum bearing test facility. These properties are compared to existing state-of-the-art space lubricants.