Mullite+CAS Bond Coat for Environmental Barrier Coatings for Si-Based Ceramics

Current environmental barrier coatings (EBCs) for silicon-based ceramics consist of a bond coat and a top coat. Mullite bond coat modified by adding low CTE glass ceramics, such as BSAS (xBaO.1xSrO.Al2O3.2SiO2) or CAS (CaO.Al2O3.2SiO2), was developed in the NASA Enabling Propulsion Materials (EPM) Program. EBCs based on mullite+CAS bond coat were characterized using high steam thermal cycling test and high steam isothermal thermogravemitry (TGA) at 1225 C - 13,000 C. The Mullite+CAS bond coat showed far superior durability compared to mullite bond coat, due to enhanced crack resistance. A BSAS top coat provided further improved durability compared to EBCs with a yttria-stabilized zirconia (YSZ) top coat. Still further improvement in the durability was achieved by adding a silicon bond coat between the mullite and the substrate. However, the silicon/mullite+CAS/BSAS EBC showed inferior long-term durability compared to the current state-of-the art EBC (silicon/mullite+BSAS/BSAS EBC), presumably due to the higher CAS-silica chemical reactivity.