Mode I, Mode II, and Mixed-Mode Fracture of Plasma-sprayed Thermal Barrier Coatings at Ambient and Elevated Temperatures

The mixed-mode fracture behavior of plasma-sprayed ZrO2-8 wt% Y2O3 thermal barrier coatings was determined in air at 25 and 1316 C in asymmetric four-point flexure with single edge v-notched beam (SEVNB) test specimens. The mode I fracture toughness was found to be K(sub Ic) = 1.15 plus or minus 0.07 and 0.98 plus or minus 0.13 MPa the square root of m, respectively, at 25 and 1316 C. The respective mode II fracture toughness values were K(sub IIc) = 0.73 plus or minus 0.10 and 0.65 plus or minus 0.04 MPa the square root of m. Hence, there was an insignificant difference in either K(sub Ic or K(sub IIc) between 25 and 1316 C for the coating material, whereas there was a noticeable distinction between K(sub Ic) and K(sub IIc), resulting in K(sub IIc) per K(sub Ic) = 0.65 at both temperatures. The empirical mixed-mode fracture criterion best described the coatings' mixed-mode fracture behavior among the four mixed-mode fracture theories considered. The angle of crack propagation was in reasonable agreement with the minimum strain energy density criterion. The effect of the directionality of the coating material in on K(sub Ic) was observed to be insignificant, while its sintering effect at 1316 C on K(sub Ic) was significant.