Experimental Investigation of a Graphite-Composite Intertank Section for a Reusable Launch Vehicle

The use of graphite-composites as primary structure is essential for the development of a cost effective single-stage-to-orbit reusable launch vehicle (RLV). A full-scale segment of a graphite-composite intertank was designed and fabricated by an industry team and tested at NASA Langley Research Center as a part of the RLV technology development program. The intertank test component was approximately 3.0 m long by 6.7 m wide and included slightly less than a 90deg section of a cylindrical intertank. The test article was fabricated using graphite-bismaelimide composite material and consisted of a hat-stiffened skin with five ring frames. The stiffeners were secondarily bonded to the panel skin and the ring frames were mechanically attached. The test article was loaded to failure with a uniform compression load applied by 21 individually controlled hydraulic actuators. Resistance strain gages, linear variable differential transformers and video cameras were used to measure and record the test results. A linear f d t e element analysis of the test article and test fixture was performed. The test results verified the structural integrity cf the intertank test article up to the design limit load. However, the test article failed in general skin buckling between the ring frames at a load 1.08 times design limit load. This load was considerably lower than the expected failure load. The cause of premature failure is being investigated. Good correlation of the test and analysis results was obtained for loads up to the design limit load.