Sintering and Fracture Behavior of Plasma-sprayed Thermal Barrier Coatings

Thermal barrier coatings will be more aggressively designed to protect gas turbine engine hot-section components in order to meet future engine higher fuel efficiency and lower emission goals. There is a need to characterize the fundamental sintering and fracture behavior of the current ZrO2-(7 to 8)wt%Y2O3 coating, in order to fully take advantage of the coating capability. In addition, a thorough evaluation of the coating behavior and temperature limits will be useful for more accurately assessing the benefit gained from future advanced coating systems. In this study, the sintering behavior of plasma-sprayed ZrO2-8wt%Y2O3 coatings was systematically investigated as a function of temperature and time using a dilatometer in the temperature range of 1200-1500 C. The coating sintering kinetics obtained by dilatometry were compared with the coating thermal conductivity increase kinetics, determined by a steady-state laser heat-flux testing approach, under high temperature and thermal gradient sintering conditions. The mode I, mode II, and mixed mode I-mode II fracture behavior of as-processed and sintering-annealed coatings was determined in asymmetric flexure loading at ambient and elevated temperatures in order to evaluate the coating sintering effects on the fracture envelope of K(sub I) versus K(sub II). The coating thermal conductivity cyclic response associated with the interface delamination of the coating systems under simulated engine heat-flux conditions will be discussed in conjunction with the sintering and fracture testing results.