Development of DMBZ-15 High-Glass-Transition-Temperature Polyimides as PMR-15 Replacements Given R&D 100 Award

PMR-15, a high-temperature polyimide developed in the mid-1970s at the NASA Lewis Research Center,1 offers the combination of low cost, easy processing, and good high-temperature performance and stability. It has been recognized as the leading polymer matrix resin for carbon-fiber-reinforced composites used in aircraft engine components. The state-of-the-art PMR-15 polyimide composite has a glass-transition temperature (Tg) of 348 C (658 F). Since composite materials must be used at temperatures well below their glass-transition temperature, the long-term use temperatures of PMR-15 composites can be no higher than 288 C (550 F). In addition, PMR-15 is made from methylene dianiline (MDA), a known liver toxin. Concerns about the safety of workers exposed to MDA during the fabrication of PMR-15 components and about the environmental impact of PMR-15 waste disposal have led to the industry-wide implementation of special handling procedures to minimize the health risks associated with this material. These procedures have increased manufacturing and maintenance costs significantly and have limited the use of PMR-15 in commercial aircraft engine components.