Material Interactions with Solar Wind Ion Environments

Solar wind composition is dominated by hydrogen (approx.96%) and helium (approx.3 to 4%) with a minor fraction (less than or equal to 1%) of heavy ions. Hydrogen (helium) ions impact spacecraft surfaces with energies from 0.5 to 5 keV (1.8 to 21 keV) due to variations in solar wind velocity from 300 km/s to 1000 km/sec with extremes of a few 10 s keV during periods of extremely high solar wind velocity exceeding 1000 km/sec. Mean impact energies are typically on the order of approximately 1 keV and 4 keV for hydrogen ions and helium ions, respectively. These energies are typically of the peak of the energy dependent light ion sputter yields for hydrogen and helium on many metals. In addition, light ions with kilovolt energies have been shown to produce blister (or exfoliation) damage to metal surfaces due to formation of high pressure gas bubbles within the materials when exposed to ion fluences on the order of 10(exp 16 to (10(exp 17 ions/sq cm. A number of spacecraft designs for current and future missions include gossamer polymer structures with thin metallic reflection coatings to shield instruments from the Sun or solar sail propulsion systems for use in a variety of locations in the inner solar system from 0.5 to 1 AU. In addition, there is interest in designing spacecraft for solar physics missions requiring operations as close to the Sun as 0.16 to 0.2 AU. Integrity of the metallic coatings is critical in many of these applications since degradation will result in modification of material thermal properties or exposure of polymers to solar UV photons which can compromise mission requirements. This paper will evaluate the relative contributions of sputtering and blister formation to material degradation in solar wind environments over a range of radial distances from the Sun to demonstrate where solar wind environments become important for materials selection. We will first review the physics and results from laboratory measurements of light ion sputtering, blistering, and exfoliation of metallic surfaces to establish the order of magnitude ion fluence required for significant surface damage. Solar wind ion fluence environments will then be evaluated due to variations in solar wind conditions as a function of solar cycle for varying distances from the Sun using models for radial variations in solar wind ion number density, temperature, and velocity to determine where sputtering and blistering is most likely to be an issue. Finally, ion fluence statistics for varying radial distances from the Sun will be shown to establish the mission duration and radial distances from the Sun where missions will encounter sufficient ion fluence to exhibit damage to metallic surfaces.