Compositional Pathways and Capillary Effects during Early-stage Isothermal Precipitation in a Nondilute Ni-Al-Cr Alloy

For a Ni-5.2 Al-14.2 Cr at.% alloy with moderate solute supersaturations, the compositional pathways, as measured with atom-probe tomography, during early to later stage y'(LI2)-precipitation (R = 0.45-10 nm), aged at 873 K, are discussed in light of a multi-component coarsening model. Employing nondilute thermodynamics, detailed model analyses during quasistationary coarsening of the experimental data establish that the y/y' interfacial free-energy is 22- 23+/-7 mJ/sq m. Additionally, solute diffusivities are significantly slower than model estimates. Strong quantitative evidence indicates that an observed y'-supersaturation of Al results from the Gibbs-Thomson effect, providing the first experimental verification of this phenomenon. The Gibbs-Thomson relationship, for a ternary system, as well as differences in measured phase equilibria with CALPHAD assessments, are considered in great detail.