Evaluation of a Highly Anticlastic Panel with Tow Overlaps

A rectangular, variable-stiffness panel with tow overlaps was manufactured using an advanced tow placement machine. The cured panel had large anticlastic imperfections, with measured amplitudes of over two times the average panel thickness. These imperfections were not due to the overall steered-fiber layup or the tow overlaps, but instead resulted from local asymmetries in the laminate that were caused by a manufacturing oversight. In the nominal panel layup, fiber angles vary linearly from 60 degrees on the panel axial centerline to 30 degrees on the parallel edges. A geometrically nonlinear analysis was performed with a -280 degree Fahrenheit thermal load to simulate the postcure cooldown to room temperature. The predicted geometric imperfections correlated well with the measured panel shape. Unique structural test fixtures were then developed which greatly reduced these imperfections, but they also caused prestresses in the panel. Surface imperfections measured after the panel was installed in the test fixtures were used with nonlinear finite element analyses to predict these fixturing-induced prestresses. These prestresses were also included in structural analyses of panel end compression to failure, and the analytical results compared well with test data when both geometric and material nonlinearities were included.