Nonlinear Spring Finite Elements for Predicting Mode I-Dominated Delamination Growth in Laminated Structure with Through-Thickness reinforcement

One particular concern of polymer matrix composite laminates is the relatively low resistance to delamination cracking, in particular when the dominant type of failure is mode I opening. One method proposed for alleviating this problem involves the insertion pultruded carbon pins through the laminate thickness. The pins, known as z-pins, are inserted into the prepreg laminate using an ultrasonic hammer prior to the curing process, resulting in a field of pins embedded normal to the laminate plane as illustrated in Figure. 1. Pin diameters range between 0.28-mm to 0.5-mm and standard areal densities range from 0.5% to 4%. The z-pins are provided by the manufacturer, Aztex(Registered TradeMark) , in a low-density foam preform, which acts to stabilize orientation of the pins during the insertion process [1-3]. Typical pin materials include boron and carbon fibers embedded in a polymer matrix. A number of methods have been developed for predicting delamination growth in laminates reinforced with z-pins. During a study on the effect of z-pin reinforcement on mode I delamination resistance, finite element analyses of z-pin reinforced double cantilever beam (DCB) specimens were performed by Cartie and Partridge [4]. The z-pin bridging stresses were modeled by applying equivalent forces at the pin locations. Single z-pin pull-out tests were performed to characterize the traction law of the pins under mode I loading conditions. Analytical solutions for delamination growth in z-pin reinforced DCB specimens were independently derived by Robinson and Das [5] and Ratcliffe and O'Brien [6]. In the former case, pin bridging stresses were modeled using a distributed load and in the latter example the bridging stresses were discretely modeled by way of grounded springs. Additionally, Robinson and Das developed a data reduction strategy for calculating mode I fracture toughness, G(sub Ic), from a z-pin reinforced DCB specimen test [5]. In both cases a traction law similar to that adopted by Cartie and Partridge was used to represent z-pin failure under mode I loading conditions. In the current work spring elements available in most commercial finite element codes were used to model z-pins. The traction law used in previous analyses [4-6] was employed to represent z-pin damage. This method is intended for and is limited to simulating z-pins in composite laminate structure containing mode I-dominated delamination cracking. The current technique differs from previous analyses in that spring finite elements (available in commercial codes) are employed for simulating zpins, reducing the complexity of the analysis construction process. Furthermore, the analysis method can be applied to general structure that experiences mode I-dominated delamination cracking, in contrast to existing analytical solutions that are only applicable to coupon DCB specimens.