Oxidation of ZrB2 SiC TaSi2 Materials at Ultra High Temperatures

ZrB2 - 20v% SiC - 20v% TaSi2 was oxidized in stagnant air for ten minute cycles for times up to 100 minutes at 1627 C and 1927 C. The sample oxidized at 1627 C showed oxidation resistance better than that of the standard ZrB2 - 20v% SiC. The sample oxidized at 1927 C, however, showed evidence of liquid phase formation and complex oxidation products. The sample exposed at 1927 C was analyzed in detail by scanning electron microprobe and wavelength dispersive spectroscopy to understand the complex oxidation and melting reactions occurring during exposure. The as hot-pressed material shows the formation of a Zr(Ta)B2 phase in addition to the three phases in the nominal composition already noted. After oxidation, the TaSi2 in the matrix was completely reacted to form Ta(Zr)C. The layered oxidation products included SiO2, ZrO2, Ta2O5, and a complex oxide containing both Zr and Ta. Likely reactions are proposed based on thermodynamic phase stability and phase morphology.