Improved Starting Materials for Back-Illuminated Imagers

An improved type of starting materials for the fabrication of silicon-based imaging integrated circuits that include back-illuminated photodetectors has been conceived, and a process for making these starting materials is undergoing development. These materials are intended to enable reductions in dark currents and increases in quantum efficiencies, relative to those of comparable imagers made from prior silicon-on-insulator (SOI) starting materials. Some background information is prerequisite to a meaningful description of the improved starting materials and process. A prior SOI starting material, depicted in the upper part the figure, includes: a) A device layer on the front side, typically between 2 and 20 m thick, made of p-doped silicon (that is, silicon lightly doped with an electron acceptor, which is typically boron); b) A buried oxide (BOX) layer (that is, a buried layer of oxidized silicon) between 0.2 and 0.5 m thick; and c) A silicon handle layer (also known as a handle wafer) on the back side, between about 600 and 650 m thick. After fabrication of the imager circuitry in and on the device layer, the handle wafer is etched away, the BOX layer acting as an etch stop. In subsequent operation of the imager, light enters from the back, through the BOX layer. The advantages of back illumination over front illumination have been discussed in prior NASA Tech Briefs articles.