Cyclic Engine Test of Cast Vitallium Turbine Buckets - I

An investigation was conducted to correlate the engine service performance of cast Vitallium turbine buckets with standard laboratory metallurgical data. Data were obtained from four I-40 turbine wheels of Timken alloy with cast Vitallium buckets. In order to accelerate bucket deterioration, the turbine wheels were subjected to 20-minute cycles consisting of 5 minutes at idle and 15 minutes at rated speed. A bucket broke on the first wheel during cycle 22 after 7 hours and 20 minutes. The broken bucket was replaced and during the third cycle after the replacement a second bucket broke after a total running time of 8 hours and 12 minutes, The first bucket failure on the second wheel occurred during cycle 29 after 9 hours and 28 minutes; no further failure occurred during 66 additional cycles. Total running time on this wheel was 31 hours and 40 minutes. The third wheel was run for 229 cycles (76 hr and 20 min, total running time) without a. failure. The fourth wheel was operated for 105 cycles (35 hr, total running time) without a failure. Examination of the bro?en buckets indicated that the failures were probably due to fatigue, Massive eutectic areas that existed near the trailing edge probably contributed to the low fatigue strength.