4-Vinyl-1,3-Dioxolane-2-One as an Additive for Li-Ion Cells

Electrolyte additive 4-vinyl-1,3-dioxolane-2-one has been found to be promising for rechargeable lithium-ion electrochemical cells. This and other additives, along with advanced electrolytes comprising solutions of LiPF6 in various mixtures of carbonate solvents, have been investigated in a continuing effort to improve the performances of rechargeable lithium-ion electrochemical cells, especially at low temperatures. In contrast to work by other researchers who have investigated the use of this additive to improve the high-temperature resilience of Li-ion cells, the current work involves the incorporation of 4-vinyl-1,3-dioxolane-2-one into quaternary carbonate electrolyte mixtures, previously optimized for low-temperature applications, resulting in improved low-temperature performance. The benefit afforded by 4-vinyl-1,3- dioxolane-2-one can be better understood in the light of relevant information from a number of prior NASA Tech Briefs articles about electrolytes and additives for such cells. To recapitulate: The loss of performance with decreasing temperature is attributable largely to a decrease of ionic conductivity and the increase in viscosity of the electrolyte. What is needed to extend the lower limit of operating temperature is a stable electrolyte solution with relatively small lowtemperature viscosity, a large electric permittivity, adequate coordination behavior, and appropriate ranges of solubilities of liquid and salt constituents. Whether the anode is made of graphitic or non-graphitic carbon, a film on the surface of the anode acts as a solid/electrolyte interface (SEI), the nature of which is critical to low-temperature performance. Desirably, the surface film should exert a chemically protective (passivating) effect on both the anode and the electrolyte, yet should remain conductive to lithium ions to facilitate intercalation and de-intercalation of the ions into and out of the carbon during discharging and charging, respectively. The additives investigated previously include alkyl pyrocarbonates. Those additives help to improve low-temperature performances by giving rise to the formation of SEIs having desired properties. The formation of the SEIs is believed to be facilitated by products (e.g., CO2) of the decomposition of these additives. These decomposition products are believed to react to form Li2CO3-based films on the carbon electrodes. The present additive, 4-vinyl-1,3-dioxolane-2-one, also helps to improve lowtemperature performance by contributing to the formation of SEIs having desired properties, but probably in a different manner: It is believed that, as part of the decomposition process, the compound polymerizes on the surfaces of carbon electrodes.