Covering a Crucible with Metal Containing Channels

In a procedure that partly resembles the lost-wax casting process, a crucible made of a brittle material (ceramic, quartz, or glass) is covered with a layer of metal containing channels. The metal cover and the channels can serve any or all of several purposes, depending upon the application: Typically, the metal would serve at least partly to reinforce the crucible. The channels could be used as passages for narrow objects that could include thermocouples and heat-transfer strips. Alternatively or in addition, channels could be used as flow paths for liquid or gaseous coolants and could be positioned and oriented for position- or direction-selective cooling. In some cases, the channels could be filled with known gases and sealed so that failure of the crucibles could be indicated by instruments that detect the gases. The process consists of three main steps. In the first step, a pattern defining the channels is formed by wrapping or depositing a material in the desired channel pattern on the outer surface of the crucible. The pattern material can be a plastic, wax, low-ash fibrous material, a soluble material, or other suitable material that can subsequently be removed easily. In a proof-of-concept demonstration (see figure), the crucible was an alumina cylinder and the mold material was plastic tie-down tape. In the second step, the patterned crucible is coated with metal. In one variation of the second step, a very thin layer containing or consisting of an electrically conductive material (e.g., gold, silver, or carbon) is painted or otherwise deposited on the mold-covered crucible, then the covering metal required for the specific application is electrodeposited on the very thin conducting layer. In another variation of the second step, the metal coat is formed by chemical vapor deposition. In the proof-of-concept demonstration, a layer of nickel 0.003 in. ( 0.08 mm) thick was electrodeposited. In the third step, the patterned material is removed. This is generally done by heating the crucible assembly until the patterned material melts and runs out, vaporizes, and/or decomposes to an ash, leaving the channels. Alternatively, if the patterned material is soluble, it can be removed by use of a suitable solvent. In the proof-of-concept demonstration, the tape was burned away by heating the assembly to a temperature of 600 C.