Adhesive Wear of Rollers in Vacuum

This work was done to support NASA's James Webb Space Telescope that is equipped with a Near Infrared Camera and Spectrograph and Micro Shutter Assembly (MSA). A MSA mechanism's qualification test in cryogenic vacuum at 30deg K for 96K cycles resulted in roller wear and formation of some debris. Lab tests in vacuum were conducted at NASA Glenn Research Center (GRC) to understand the wear of Ti6Al4V mated with 440F steel rollers. Misalignment angle was found to have the most significant effect on debris formation. At misalignment angle of 1.4deg, significant amount of wear debris were formed within 50,000 cycles. Very few wear particles were found for a zero misalignment angle, and the total wear was small even after 367,000 cycles. The mode of wear in all the tests was attributed to adhesion, which was clearly evident from video records as well as the plate-like amalgamated debris material from both rollers. The adhesive wear rate was found to be approximately proportional to the misalignment angle. The wear is a two-way phenomenon, and the mixing of both roller materials in wear debris was confirmed by x-ray fluorescence (XRF) and EDX spectra. While there was a net loss of mass from the steel rollers, XRF and energy dispersive x-ray (EDX) spectra showed peaks of Ti on steel rollers, and peaks of Fe on Ti rollers. These results are useful for designers in terms of maintaining appropriate tolerances to avoid misalignment of rolling elements and the resulting severe wear