Flexural Fatigue Behavior of an EBC CMC Composite System In Air and Steam at High Temperature

Both coated and uncoated SiCSiC ceramic matrix composite (CMC) samples were tested in flexure under sustained peak low cycle fatigue (SPLCF) conditions in air or steam at elevated temperatures. The SiCSiC composites were reinforced with 2-D plies of boron nitride coated Hi-Nicalon Type-S SiC fibers which were woven as 5 harness satin (5HS) cloth. The composites were densified by chemical vapor infiltration (CVI) followed by slurry melt infiltration (SMI). A multilayer barium strontium aluminosilicate (BSAS) coating was applied to the samples by a plasma spray method. Fatigue loading limits were determined from monotonic flexure tests at room temperature and 1200oC. Stress levels under the proportional limit of the composite material were selected for the SPLCF tests. After cyclic testing, the composites were evaluated to determine crack propagation and failure modes in the coated and uncoated composites. Microstructural examination was used to identify coating degradation and failure modes of the EBCCMC system.