Potential Weight Benefits of IM7/8552 Hybrid Thin-Ply Composites for Aircraft Structures

Composite materials have increasingly been used for aerospace applications due to improved performance and reduced weight compared to their metallic counterparts. Inclusion of thin-ply material, plies with cured thickness half or less than standard-ply composites, have potential to improve performance and reduce structural weight further. The effect of thin-ply material on the weight of aircraft structure was investigated by examining wing cover weight reduction. To minimize the effects on manufacturing due to using thin plies, hybrid laminates were examined that used thin ±45-degree plies to replace their standard-ply counterparts in laminates. Compression after impact (CAI) tests were conducted to examine the possible weight savings that could be gained by increasing the design allowables that were used to size the wing upper cover of a semi-span test article. A large increase in CAI strength was observed for quasi-isotropic hybrid laminates, whereas less improvement was seen for hard hybrid laminates such as found in the wing cover. For laminates design by CAI strength, weight savings of about 13% were found using the hybrid hard laminates compared to the standard-ply laminates. Whether similar weight savings could be expected for structure sized using tension after impact allowables will have to be investigated further. Notched specimens were tested to examine possible weight savings using hybrid laminates in regions that are sized using discrete source damage requirements. As expected, the hybrid laminate had marginal improvements over the standard-ply laminate for compression with a notch present. The hybrid laminate, however, exhibited about 20% lower strength than the standard-ply laminate counterpart for tension with a notch. The failure mode of the hybrid specimens was a brittle, self-similar crack, which differs from the standard-ply specimens that failed by significant amounts of delamination and fiber splitting. In light of the apparent reduction in notched tensile strength, additional investigation is required to assess the use of hybrid laminates for areas containing discrete source damage, and their effect on weight of such regions.