Full-Scale Test and Analysis Results of a PRSEUS Fuselage Panel to Assess Damage-Containment Features

An area that shows promise in enhancing structural integrity of aircraft and aerospace structures is integral stitched composite technology. The most recent generation of this technology is the Pultruded Rod Stitched Efficient Unitized Structure (PRSEUS) concept. The goal of the PRSEUS concept is to provide damage-containment capability for composite structures while reducing overall structural weight. The National Aeronautics and Space Administration, the Boeing Company, and the Federal Aviation Administration (FAA) have partnered in an effort to assess the damage-containment features of a full-scale curved PRSEUS panel using the FAA Full-Scale Aircraft Structural Test Evaluation and Research facility. The background, test plan, fixture modifications, pre-test analysis, and planned experimental procedure were presented at the 2011 Aircraft Airworthiness and Sustainment Conference. This follow-on paper and presentation will provide details of the experimental procedure, test results, nondestructive inspection results, and preliminary test analysis comparison. The test program included three phases of loading and inspections: Phase I, as-built; Phase II, with barely visible impact damage (BVID); and Phase III, with a two-bay notch severing the central stiffener. Axial tension, internal pressure, and combined axial tension and internal pressure load conditions were applied during each phase using load levels that demonstrate compliance with the strength, deformation, and damage-tolerance requirements of Title 14 Code of Federal Regulations Part 25. Pressure loads were based on an operating pressure of 9.2 psi, designated as 1P, and the axial loads were based on a design limit load (DLL) of 227 kip. The Phase I test results provided a baseline. First, 50 percent limit-load levels were applied for each of the three load cases to verify proper load introduction and repeatability by examining strain and displacement results. Next, three limit-load cases were applied: limit pressure of 12.2 psi (1.33 P), axial DLL of 227 kip, and combined 1P pressure and axial DLL. Linear strain and displacement results were observed in all load cases. For Phase-II testing, the panel was impacted to introduce BVID with an energy of 40 ft-lb, with the impact located between the central stringer stitch line and flange edge. The impact created non-penetrating visual damage with fiber breaks and delamination between the skin and stringer flange. Limit-load conditions were applied followed by pressure overload of 18.4 psi (2P) and ultimate load conditions, defined as 1.5 times DLL. Inspections were performed after each load case; no damage growth was observed. For Phase-III testing, a two-bay notch was machined severing the central stiffener. The panel was then subjected to limit-load conditions, followed by combined 1P pressure while increasing axial tension load to catastrophic failure. As limit combined loads were approached, damage initiation was observed in the form of 45? splitting at 1P + 79% DLL. Axial loading was increased to 1P + 150 percent DLL causing damage to propagate to the adjacent stringer flanges. Damage was contained within the two-bay region by the stitching rows up to 1P + 176% DLL. Axial load was further increased until catastrophic failure, when a stringer rod failed at 1P + 192% DLL. These test results further verify the damage containment features of the PRSEUS concept and suggest its appropriateness for future flight vehicles.