Microstructure-focused Durability and Damage Tolerance Research at NASA Langley

Currently, there are two national challenge problems that guide much of the research in durability and damage tolerance at NASA Langley. The first, Airframe Digital Twin, is a concept that combines as-built vehicle components, as-experienced loads and environments, and other vehicle-specific characteristics to enable ultrahigh fidelity modeling of aircraft and spacecraft throughout their service lives. The second, Materials Genome Initiative, is an analog to the Human Genome Project, and is intended to improve the rate at which materials scientists can discover, understand fundamental physics, and improve material systems.

This presentation will highlight several research projects ongoing at NASA Langley that are in support of the above challenge problems. Two of those topics will be the subject of detailed discussion. First, investigations of microstructurally-small fatigue cracking (MSFC) in Al-2Cu and Al-4Cu, fabricated in-house, will be presented. Single- and oligo-crystals of Al-Cu specimens were loaded in uniaxial fatigue, while high-resolution in-situ measurements of deformation were made using image correlation (IC) in a scanning-electron microscope (SEM). The Al-Cu specimens were then replicated as crystal plasticity finite element models (CPFEM), where evolution of slip localization near grain boundaries was computed. Comparison among experiment and CPFEM is made. In addition, XRay diffraction measurements of the as-fabricated specimens were carried out, where direct measurements of the embedded copper precipitates were made, and their influence on growing MSFCs were directly observed. The second main topic will illustrate ongoing work in the area of so-called damage-sensing particles. In this work, shape-memory alloys are embedded in an aluminum alloy matrix. Upon the propagation of a fatigue crack, these particles undergo a strain-induced phase transformation which is detected using an acoustic sensor, providing real-time information on propagating cracks. Experiments and simulations regarding the development of this system will also be detailed.