Residual Stress Measurements of Ni-base Superalloys through Neutron Diffraction

Linear friction welding (LFW) is being considered for joining single crystal to polycrystalline nickel-base alloys for advanced high temperature gas turbine disks. Unfortunately, the transient thermal cycle during the welding generates undesirable residual stresses. Additionally, upon thermal treatment to relieve these residual stresses the weld joints often crack. To understand this issue, state-of-the-art neutron diffraction was performed near weld joints to quantify the residual stresses created by varying linear friction weld conditions. The residual stresses were measured along three orthogonal axes in both the polycrystalline LSHR and single crystal SC-180 alloys. Residual stress measurements using a contour method were used to compare the calculations obtained by neutron diffraction. The results suggest high residual stresses can be successfully reduced using both pre- and post-weld processing steps. Moreover, the effect of grain size and pre-heat temperatures on the LFW process were explored.