Thermal Expansion Coefficients of Ca2Y8(SiO4)6O2 and Ca2Yb8(SiO4)6O2 Apatite-type Silicates

High temperature X-ray diffraction (XRD) scans of Y2Si2O7 and Yb2Si2O7 reactions with calcium-magnesium-aluminosilicates (CMAS) were utilized to determine thermal expansion coefficients (CTEs) of Ca2Y8(SiO4)6O2 and Ca2Yb8(SiO4)6O2 apatite materials. In order to validate these measurements, the CTEs of Y2Si2O7, Yb2Si2O7 and SiO2 were also determined from the same scans. The directional CTEs for γ-Y2Si2O7 were determined to be αa=5.84×10-6/K, αb=6.81×10-6/K and αc=0.81×10-6/K, and β-Yb2Si2O7 was determined to have values of αa=6.89×10-6/K, αb=4.81×10-6/K and αc=2.78×10-6/K. The average CTEs of γ-Y2Si2O7 and β-Yb2Si2O7 were determined to be 4.5×10-6/K and 4.7×10-6/K, respectively, which agreed with previous analyses. Ca2Y8(SiO4)6O2 exhibited directional CTEs of αa=9.36×10-6/K and αc=7.95×10-6/K (averaged between two sets of data), whereas Ca2Yb8(SiO4)6O2 had values that were very similar (αa=9.63×10-6/K, αc=7.45×10-6/K). Both results for the Ca2RE8(SiO4)6O2 apatites correlated well with the limited data on apatite-type silicates available in literature.