Melting and Crystallization Behavior of CaO-MgO-Al2O3-SiO2 Silicates Relevant to Turbine Engine Applications

The melting and crystallization behavior of four quaternary CaO-MgO-Al2O3-SiO2(CMAS) silicates were investigated. The CaO:SiO2 ratios of these systems were based on various terrestrial sources of ingested particles relevant to gas turbine engine operating environments. Melting behavior was characterized using differential scanning calorimetry, and high temperature intrinsic crystallization products were determined by furnace heat treatments of the glasses at 1200°C, 1300°C, and 1400°C. The silicates exhibited a wide range of melting temperatures from ~1240°C up to ~1500°C, with most of the compositions exhibiting incongruent melting behavior. High temperature crystallization products included CaSiO3,CaAl2Si2O8, Ca2MgSi2O7, and Ca(Mg,Al)Si2O6, although SiO2 was the only crystalline phase observed at 1400°C.