Results from Two Full-Scale Hawker 4000 Fuselage Drop Tests

In the spring of 2022, NASA Langley Research Center (LaRC) conducted two full-scale drop tests on a Hawker 4000 partial fuselage structure for the evaluation of composite material response under dynamic impact loading conditions. The specific objectives of the tests were to induce dynamic composite damage
initiation and progression and in primary structure and to understand the nature of the failure modes. The tests were conducted via dividing the fuselage hardware into three smaller sections. Dynamic drop tests were conducted on the forward and aft portions of the fuselage under different dynamic loading
conditions, while the middle section was reserved for materials testing. Both tests were conducted by dropping the test articles from a height of 14 feet with significant amounts of pitch, which was added to initiate damage in specific regions of the structure. The test articles were ballasted then instrumented with
accelerometers at various locations and speckle-coated on both exterior sides with a black and white stochastic pattern for use with three-dimensional digital image correlation (3D-DIC). In addition, the interior belly portion of the forward section test article was also speckle-coated, which was intended to capture deformations on the belly of the test article from the interior at impact. The interior of the aft section test article was not speckle-coated. Prior to testing, bow-tie markers were applied at various locations for use in marker tracking, to measure impact conditions such as vertical impact velocity and pitch.

In this report, a partial summary of the data collected from the tests is presented. The data was primarily in the form of accelerometers to measure impact acceleration and 3D-DIC to measure deformation and failure onset and propagation. Post-test inspections revealed the primary damage mechanism was fiber cracking and delamination primarily in and around the area that contacted the impact surface. Acceleration pulse shapesin the ballast locations were trapezoidal in nature and ranged between 10 g and 40 g, depending on the location and test.