Development of Luminescence Lifetime-Based Surface Temperature Mapping for Environmental Barrier Coatings

Luminescence lifetime-based temperature mapping for thermal barrier coatings (TBCs) has been previously demonstrated up to temperatures approaching 1200 °C. Advantages of this method include insensitivities to reflected radiation and emissivity uncertainties. Because of a push towards greater efficiency turbine engine operation using higher turbine inlet temperatures, there is an ongoing movement from TBC-coated superalloy turbine engine components to SiC/SiC ceramic matrix composite components protected by environmental barrier coatings (EBCs). The useful application of luminescence lifetime-based temperature mapping to EBCs requires a significant increase in high temperature capability from below 1200 °C up into the 1300 to 1500 °C temperature range where the much higher background thermal radiation is a challenging issue. In addition, the luminescing sensing layer must exhibit thermochemical compatibility with the EBC. To meet these requirements, Er-doped Y2SiO5 was selected as the luminescing sensor layer material both for its enhanced temperature sensitivity above 1300 °C and its compatibility with rare-earth disilicate EBC topcoats. Both localized spot temperature measurements as well as luminescence lifetime imaging-based temperature mapping were demonstrated up to 1560 °C for Er-doped Y2SiO5 disks. In addition, temperature mapping capability was demonstrated from a 15 µm thick Er-doped Y2SiO5 layer at the surface of a Sc2Si2O7 based EBC topcoat. Both localized spot and temperature mapping by luminescence lifetime imaging were demonstrated up to 1380 °C (upper temperature limit of this slurry-based layered EBC) with excellent suppression of background thermal radiation and no degradation of the Er-doped Y2SiO5 temperature sensing surface layer. The source of the novel enhanced temperature sensitivity above 1300 °C will be discussed as well as a path towards compatibility between sensing layer and EBC topcoat to higher temperatures.