Exploring the Effect of EBC Composition on CMAS Wetting Behavior

Rare-earth disilicate (REDS) materials are existing materials used in environmental barrier coating (EBC) for the protection of structural materials in the hot-section of turbine engines. REDS interactions with molten calcium-magnesium-aluminosilicate (CMAS) debris are of interest to understand molten CMAS attack and improve CMAS mitigation strategies. This work assesses the effect of REDS composition on CMAS wetting by investigating wetting angle, spreading, and reactivity. Freestanding atmospheric plasma spray (APS) REDS coatings (for RE = Y, La, Nd, Gd, Yb, Lu) were exposed to 10 mg of CMAS (Ca33-Mg9-Al13-Si45 in single cation mol%) in stagnant lab air at 1250C. APS YbDS was compared to a dense spark plasma sintered (SPS) phase-pure Yb2Si2O7 and a nominal 20 vol% phase-mixture of Yb2SiO5 in Yb2Si2O7 (20YbMS/YbDS). CMAS mass was held constant but specimen surface areas varied, yielding a range of loading between ~6 and 10 mg/cm2. CMAS was loaded as a cylindrical rod atop the specimen surface, polished to 4000 grit, and heated to temperature in a Linseis L74/HS/1700 heating microscope. The heating microscope measured the evolution of molten CMAS diameter, height, and contact angle. Molten CMAS diameter at 1150C and contact angle measurements after two hours of exposure at 1250C yielded a positive trend with rare-earth cation size. There was no statistically significant difference in CMAS wetting behavior between SPS YbDS and 20YbMS/YbDS. Post-exposure specimens were examined in plan view and cross-section with XRD, SEM, and EDS. CMAS spreading was cross-examined using plan view SEM, while reactivity utilized plan view XRD and cross-sectional SEM/EDS.