Pull-off Behavior of Stitched Composite T-Joints

T-joints are key structural elements that connect opposing surfaces, thereby providing the load path between flat or curved panels (i.e., upper and lower wing skins) and transverse components (i.e., stiffeners). Due to the low interlaminar strength of polymer matrix composites and their geometrical discontinuities, these joints are vulnerable to pull-off loads. To address these issues, through-thickness reinforcements can be employed to enhance the interlaminar capability of these type of joints. In this study, T-joints were manufactured using through-thickness stitching in dry carbon preforms and cured using the vacuum-assisted resin transfer molding (VARTM) process. Stitched and unstitched T-joints were tested under pull-off loading conditions, and surface strain fields were obtained using a 3D digital image correlation system. The ultimate load, displacement, and absorbed energy of the stitched T-joints were greater than their unstitched counterparts by approximately 16%, 34%, and 58%, respectively. Failure mechanisms were identified by examining fracture surfaces using optical microscopy. Results demonstrate that through-thickness stitching significantly improves the damage tolerance of T-joints, which highlights the effectiveness of stitching to enhance the structural integrity of large aerospace components.