X-Ray Diffraction Based Phase Identification in NiTiHf Shape Memory Alloys with Variable Hf Content

NiTiHf type shape memory alloys have been studied for use in high temperature actuator applications, the most studied of which is the NiTi-20Hf atomic % composition. In this study, six samples of NiTi-Hf including 20Hf, 30Hf, 35Hf, 40Hf, 45Hf, and 50Hf were evaluated by both 1D and 2D X-ray diffraction (XRD) to elucidate what phases and crystal structures were present at room temperature. Given small sample sizes and relatively large grains, multiple cross-sections were measured to increase the sampling statistics, and 2D XRD frames were collected to corroborate the 1D XRD data. Rietveld and structureless refinements were both performed, allowing for adjustments in orientation lattice constant, and structure factor. At room temperature, the primary martensitic phase in the NiTiHf alloys with 20 at% and lower Hf is a monoclinic B19’ phase (P1121/m space group). This phase was identifiable, even in small amounts, in the higher Hf samples. The primary phase in the 30 -50 at% Hf samples is an orthorhombic B33 (Cmcm space group) phase. This work supported thermal analyses indicating the phase transition paths from the two different room temperature martensitic phases to the B2 austenitic phase.