Effect of Barely Visible Impact Damage on Thermoplastic Welded Structure

Spirit Aerosystems recently conducted screening tests on thermoplastic skin/stringer panels manufactured with Automated Fiber Placement (AFP) and stamp forming which were joined using Spirit’s Co-Fusion process. Skin and stringer gauge were both set to 0.168 cm. The resulting panel design is 48 cm tall, 49 cm wide, and has 3 stringers welded at a 21.5 cm pitch. Barely Visible Impact Damage (BVID) and Residual Compressive Strength were chosen to conduct a damage tolerance study. Zee stringers, made with IM8/PEKK-FC material, were Co-Fusion welded to a T1100/TC1225 skin. Out of these 5 panels, 1 was chosen to be a BVID survey panel, 1 for pristine compressive strength determination, and 3 to be impacted to create BVID followed by testing for residual compressive strength. On the survey panel, impacts ranged in energy from 40J – 65J and dent depth measurements were conducted at 24 hours, 48 hours, and two weeks after impacting. The residual compressive strength panel failed near the predicted load of 214 MPa. For the residual compressive strength panels, BVID was created at two different mid-bay locations: 1) striking the OML coincident with the stringer and 2) striking the skin IML 2.5 cm away from the stringer flange. Pulse Echo Ultrasonic Testing was used to inspect the panels before and after creating BVID.