Biobased Polybenzoxazine Derived from Furfurylamine and Piceol with Low Cure Temperature and Advanced Properties for Composite Matrices

A novel benzoxazine made from furfurylamine, paraformaldehyde, and piceol, Bz-FA-HA, is assessed for applications in fiber reinforced (FR) composites. Piceol is a biobased phenolic compound derived from the roots of Norwegian spruce trees and contains a methyl ketone group at the para position. Bz-FA-HA is a liquid at room temperature, has a viscosity of < 1 Pa.s at temperatures above 90 °C, and a Tonset of cure at 132 °C. The carbonyl is found to react with the furan ring, yielding a crosslinking reaction, when cured above 180 °C as indicated by differential scanning calorimetry and thermogravimetric analysis coupled with Fourier transform infrared spectroscopy. Poly(Bz-FA-HA) has a Tg > 350 °C, attributed to the crosslinking reaction. Furthermore, the storage modulus is > 3 GPa, regardless of cure temperature. Poly(Bz-FA-HA) has a char yield at 800 °C of 65.0 % (62.3 % at 1000 °C), and a Tonset of decomposition of 357 °C in nitrogen. The resulting carbon formed during pyrolysis shrinks during the carbonization reaction and scanning electron microscopy imaging shows a cross-section with micro cracks. The high processability, advanced mechanical properties, and exceptional char yield make it a promising candidate as the matrix for FR composites.