The oxidation behavior of Ni-Cr-Al-2ThO2 alloys at 1093 and 1204 C.

A pack diffusion process has been developed which permits the introduction of nearly 6 wt % Al into solid solution in the near surface region of TDNiCr (Ni-20 wt % Cr-2 vol % ThO2) and Ni-20Cr. Alumina scales, adherent under cyclic heating and cooling conditions, were produced on TDNiCr-5.86Al upon exposure to an environment of 1330 N/sq m (10 torr) or 101,000 N/sq m (760 torr) air at temperatures of 1093 and 1204 C. While the same oxidation kinetics were observed in isothermal tests for Ni-14.6Cr-5.86Al as were obtained for the TDNiCr-5.86Al, the dispersion-strengthened alloy exhibited superior oxide scale adhesion during cyclic testing. At 1204 C, continuous weight gains were observed under all test conditions for TDNiCr-5.86Al, in contrast to the weight loss with time which occurred several hours after exposure of TDNiCr to an oxidizing environment. TDNiCr with an initial aluminum surface concentration of 4.95 wt % has nearly comparable oxidation resistance to the TDNiCr-5.86Al alloy.