Mach 1 oxidation of thoriated nickel chromium at 1204 C /2200 F/.

Electropolished and ground samples of TD-NiCr were exposed to a 1-atm, Mach 1 gas stream at 1204 C for times up to 50 hr. The samples were subjected to both cyclic and isothermal exposure. Weight change, metal loss, X-ray diffraction, metallographic, and electron microprobe analyses were performed. Neither surface preparation nor cyclic-against-isothermal-exposure conditions had a strong effect on the oxidation behavior of the alloy. Initially, a Cr2O3 layer was formed whose volatilization resulted in a very rapid loss of metal - more than 40 microns in the first hour. At about 1 hr, the Cr2O3 layer broke down and NiO began to cover the surface. By 5 hr, the NiO had covered the surface and the rate of loss slowed. The rate-controlling step was diffusion of Cr through NiO.