A new criterion for failure of materials by environment-induced cracking

A new criterion has been developed for predicting failure of materials by environment-induced cracking. The criterion has been developed by the use of fracture mechanics concepts and assumes that the relationship between crack-growth rate and stress intensity can be described by three separable regions of behavior as first suggested by Wiederhorn. The analytical form of the criterion relates failure time to the initial crack length and the critical crack length or alternatively, to the initial stress intensity and the fracture toughness for various conditions of stress and the environmental variables. The analytical expression is examined by the use of some experimental data on the hydrogen-induced cracking of Ti-5Al-2.5 Sn, and it is demonstrated that the expression predicts the general expected form of the relationship between the normalized stress intensity parameter and the failure time.