Axial fatigue of /0, +30, and -30 deg/6s graphite/epoxy

Results are presented for an investigation carried out on a /0, +30, and -30 deg/6s graphite/epoxy angle-ply laminate in order to characterize the overall fatigue behavior, to evaluate strength/moduli degradation due to cyclic loading, and to identify the failure modes and mechanisms. The specimen life determined from fatigue tests is measured as a function of cyclic stress amplitude for various stress ratios. Fractured specimens are sectioned and examined by conventional metallography and SEM to reveal failure modes and mechanisms. It is shown that the laminate studied is susceptible to axial fatigue failures under cyclic loading which involves both tensile and compressive mean stresses. Fracture surface observations indicate the occurrence of complex failure modes. A variety of local failure mechanisms are identified.