Effect of preload on the fatigue and static strength of composite laminates with defects

The effect of a preload cycle on the structural performance of three graphite/epoxy composite laminates was studied. The layups studied were a laminate typical of general purpose structures (L1), a laminate representative of a filament wound tank (L2), and a laminate representative of turboengine fan blades. The effects of three sizes of simulated initial defects were studied. The tests developed static strength data, fatigue to failure data, and residual static data after application of a predetermined number of fatigue cycles. For L1 specimens, there was a slight trend for the static strength to be greater for preloaded specimens. After application of cyclic loading, however, the influence of preloading was insignificant. In L2 and L3 specimens there was no consistent difference in the static or fatigue results between preloaded and nonpreloaded specimens.