Dynamic crystallization experiments bearing on the origin of textures in impact-generated liquids

Dynamic crystallization experiments on a synthetic glass of 14310 composition show that the density and distribution of crystals present at the initiation of cooling can drastically affect the texture of the crystallized product. Experiments were performed in one-atmosphere gas-mixing furnaces at an oxygen fugacity slightly below iron-wustite, and precooling crystallization, cooling history, and melt history were systematically varied. When cooled from a complete liquid, the experimental charges were porphyritic with 1-2 mm phenocrysts set in a very fine-grained matrix (less than 0.1 mm). This result suggests that 14310 did not cool from a complete melt. When cooled from a crystal-liquid mixture, the experimental charges had widely varying textures depending on the density and distribution of crystals that act as nucleation sites. It is suggested that the close spatial association of widely divergent textures in the matrices of some breccias and rocks might arise in this manner; local variations in cooling rates are not required.