Development of toughened epoxy polymers for high performance composite and ablative applications

A survey of current procedures for the assessment of state of cure in epoxy polymers and for the evaluation of polymer toughness as related to nature of the crosslinking agent was made to facilitate a cause-effect study of the chemical modification of epoxy polymers. Various conformations of sample morphology were examined to identify testing variables and to establish optimum conditions for the selected physical test methods. Dynamic viscoelasticity testing was examined in conjunction with chemical analyses to allow observation of the extent of the curing reaction with size of the crosslinking agent the primary variable. Specifically the aims of the project were twofold: (1) to consider the experimental variables associated with development of "extent of cure" analysis, and (2) to assess methodology of fracture energy determination and to prescribe a meaningful and reproducible procedure. The following is separated into two categories for ease of presentation.